AZS Brick-Refractory Brick
It is mainly used in iron blast furnace and blast furnace hot blast furnace, outside refining furnace, sliding water device, glass melting furnace and petrochemical industry furnace. AZS Brick Use It is mainly used for lining of blast furnace, hot blast furnace, electric furnace top, blast furnace, reflector and rotary kiln.
AZS brick, also named as fused cast zirconia corundum brick, whuich is widely used brick for glass kiln, it is mainly used in the upper structure of the melting tank, wall brick and bottom paving brick of work pool and feeder trough, etc.
refractory fused cast AZS Brick for Glass Melting Furnace
Application of refractory fused cast AZS Brick for Glass Melting Furnace: Refractory fused cast AZS Brick for Glass Melting Furnace is widely used in the void free configuration:electrode blocks, submerged walls, throats, and in some cases melter sidewalls. Available as well, for sidewall application, in the specific "reinforced filling" version.
The Application Of Zirconia Refractories In Glass Furnaces
The fused cast high zirconia refractories are widely used in glass furnaces, due to their good corrosion resistance and their low ability to generate defects in glass. Fused cast AZS block is made from pure alumina powder and Zircon sand (composed of 65% zirconia and 34% SiO2).
CORROSION-EROSION WEAR OF REFRACTORY BRICKS IN GLASS FURNACES
Experimental The evaluation was made in new AZS refractory bricks and AZS bricks extracted from a furnace after 4 years campaigning, Fig. 1a shows a furnace in use during the glass melting process, and the 1b indicates the placement of the samples took for this research. 2.1.
How To Select Fused Cast AZS Block For Glass Furnaces
The use of fused cast AZS expands the life of glass furnaces. The life of glass furnaces can be expanded from 11-15 months to 3-4years, even longer. The melting temperature of the glass can be increased from 1450 ℃ to 1550 ℃, even up to 1600 ℃. The glass defects are reduced and the quality of glass is improved.